DEFC不锈钢双极板的电化学行为研究
Research on electrochemical behaviour of stainless steel bipolar plate
-
摘要: 为评估金属双极板在直接乙醇燃料电池(DEFC)环境中的耐蚀性能,采用50 ℃的0.05 mol/L H2SO4+x mol/L CH3CH2OH (x=0,1,5,10,13)溶液来模拟DEFC的阳极运行环境,在该环境中对304不锈钢(304SS)的表面形貌进行表征,并对其进行极化、恒电位时间-电流密度等电化学测试.结果表明,在高浓度的乙醇腐蚀溶液中,304SS表面局部腐蚀的现象有所缓和,其耐蚀性能较好;乙醇起到减缓304SS在0.05 mol/L H2SO4溶液中腐蚀速率的作用;304SS在乙醇浓度高的DEFC运行环境中具有较高的稳定性.Abstract: In order to evaluate the corrosion resistance of metal bipolar plate in direct ethanol fuel cell (DEFC) environment, a solution of 0.05 mol/L H2SO4 +x mol/L CH3CH2OH (x=0,1,5,10,13) was used to simulate DEFC anode operating environment. In the environment, the surface morphology of 304 stainless steel (304SS) was characterized, and the electrochemical tests were carried out for polarization and constant current time-current density. The results showed that ethanol had not much effect on 304SS corrosion potential. Ethanol played a role in slowing the corrosion rate of 304SS in 0.05 mol/L H2SO4 solution. 304SS had a high stability in DEFC operating environment with high ethanol concentration.
-
Key words:
- DEFC /
- 304SS bipolar plate /
- electrochemical behaviour /
- corrosion resistance
-
-
[1]
KIMIAIE N,WEDICH K,HEHEMANN M,et al.Results of a 20 000 h lifetime test of a 7 kW direct methanol fuel cell (DMFC) hybrid system-degradation of the DMFC stack and the energy storage[J].Energy Environmental Science,2014,7(9):3013.
-
[2]
PAPADIAS D D,AHLUWALIA R K,THOMSON J K,et al.Degradation of SS316L bipolar plates in simulated fuel cell environment: Corrosion rate,barrier film formation kinetics and contact resistance[J].Journal of Power Sources,2015,273:1237.
-
[3]
AN L,ZHAO T S.Transport phenomena in alkaline direct ethanol fuel cells for sustainable energy production[J].Journal of Power Sources,2017,341:199.
-
[4]
WANG L X,KANG B,GAO N,et al.Corrosion behaviour of austenitic stainless steel as a function of methanol concentration for direct methanol fuel cell bipolar plate[J].Journal of Power Sources,2014,253:332.
-
[5]
STEIN Z,GILEADI E.Proton conductivity in mixed solvents[J].Journal of the Electrochemical Society,1985,132(9):2166.
-
[6]
王利霞,方华,孙俊才.PEMFC渗铌改性不锈钢双极板的耐蚀性研究[J].电源技术,2016,40(5):1004.
-
[7]
NAKAGAWA N,TSUJIGUCHI T,SAKURAI S,et al.Performance of an active direct methanol fuel cell fed with neat methanol [J].Journal of Power Sources,2012,219:325.
-
[8]
SINGH V B,RAY M.Effect of H2SO4 addition on the corrosion behaviour of AISI 304 austenitic stainless steel in methanol-HCl solution [J].International Journal of Electrochemical Science,2007(2):329.
-
[1]
计量
- PDF下载量: 39
- 文章访问数: 959
- 引证文献数: 0